Behavior of Mg-GAl-xSi alloys during solution heat treatment at 420 degrees C
Autore:
Lu, YZ; Wang, QD; Zeng, XQ; Zhu, YP; Ding, WJ;
Indirizzi:
Shanghai Jiao Tong Univ, Coll Mat Sci & Engn, Shanghai 200030, Peoples R China Shanghai Jiao Tong Univ Shanghai Peoples R China 200030 Peoples R China
Titolo Testata:
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
fascicolo: 2, volume: 301, anno: 2001,
pagine: 255 - 258
SICI:
0921-5093(20010331)301:2<255:BOMADS>2.0.ZU;2-7
Fonte:
ISI
Lingua:
ENG
Soggetto:
INTERMETALLIC MG2SI-AL ALLOYS; MAGNESIUM ALLOYS; MECHANICAL-PROPERTIES; TENSILE-STRENGTH; SI ALLOYS; AL-ALLOY; MICROSTRUCTURE; COMPOSITE;
Keywords:
Mg-Al-Si alloys; solution heat treatment; diffusion;
Tipo documento:
Article
Natura:
Periodico
Settore Disciplinare:
Physical, Chemical & Earth Sciences
Engineering, Computing & Technology
Citazioni:
18
Recensione:
Indirizzi per estratti:
Indirizzo: Lu, YZ Shanghai Jiao Tong Univ, Coll Mat Sci & Engn, Shanghai 200030, Peoples R China Shanghai Jiao Tong Univ Shanghai Peoples R China 200030 s R China
Citazione:
Y.Z. Lu et al., "Behavior of Mg-GAl-xSi alloys during solution heat treatment at 420 degrees C", MAT SCI E A, 301(2), 2001, pp. 255-258

Abstract

The effect of solution heat treatment at 420 degreesC on the morphology ofMg2Si particles in Mg-Al-Si alloys was investigated. The Mg2Si particles tended to be spherodized during the treatment due to the diffusion of Si atoms along the Mg2Si/Mg interface, which is benefit the mechanical propertiesof the alloys. (C) 2001 Elsevier Science B.V. All rights reserved.