Titolo:
Effect of the Mo addition on the superconducting transition temperature T-c of A15 Nb3Al
Autore:
Hwang, KY; Shinoda, T; Oya-Seimiya, Y;
Indirizzi:
Meiji Univ, Adv Mat Res & Dev Ctr, Tokyo 1918506, Japan Meiji Univ TokyoJapan 1918506 v Mat Res & Dev Ctr, Tokyo 1918506, Japan
Titolo Testata:
JOURNAL OF THE JAPAN INSTITUTE OF METALS
fascicolo: 5, volume: 64, anno: 2000,
pagine: 299 - 302
SICI:
0021-4876(200005)64:5<299:EOTMAO>2.0.ZU;2-1
Fonte:
ISI
Lingua:
JPN
Keywords:
superconducting transition temperature (T-c); A15 Nb3Al; molybdenum addition; lattice parameter;
Tipo documento:
Article
Natura:
Periodico
Settore Disciplinare:
Engineering, Computing & Technology
Citazioni:
12
Recensione:
Indirizzi per estratti:
Indirizzo: Hwang, KY Meiji Univ, Adv Mat Res & Dev Ctr, Tokyo 1918506, Japan Meiji Univ Tokyo Japan 1918506 & Dev Ctr, Tokyo 1918506, Japan
Citazione:
K.Y. Hwang et al., "Effect of the Mo addition on the superconducting transition temperature T-c of A15 Nb3Al", J JPN METAL, 64(5), 2000, pp. 299-302

Abstract

The effect of the Mo addition on the superconducting transition temperature, T-c, of the A15 Nb3Al alloy has been investigated on the basis of a general trend that T-c increases as the lattice parameter decreases for this kind of alloy series. The lattice parameter of the A15 phase decreases monotonically with increasing Mo content. T-c of the Nb-20 mol% alloys in addition of 2 to 3.5 mol%Mo becomes higher than that of the Mo-free alloy, T-c(0), and attains a peakof 14.8 K at 2 mol%Mo, which is about 2 K higher than T-c(0). For Mo contents higher than 5 mol%, the enhancing effect of Mo on the T-c of Nb3Al alloy disappears.