Titolo: SOLUBILITY OF NITROGEN IN AUSTENITIC FECRMN ALLOYS
Autore: KUNZE J; ROTHE I;
- Indirizzi:
- INST FESTKORPER & WERKSTOFFORSCHUNG DRESDEN EV DRESDEN GERMANY
- Titolo Testata:
- Steel research
fascicolo: 8,
volume: 65,
anno: 1994,
pagine: 331 - 337
- SICI:
- 0177-4832(1994)65:8<331:SONIAF>2.0.ZU;2-B
- Fonte:
- ISI
- Lingua:
- ENG
- Soggetto:
- MN-N SYSTEM; THERMODYNAMIC EVALUATION; CR-MN; TEMPERATURE;
- Tipo documento:
- Article
- Natura:
- Periodico
- Settore Disciplinare:
- Science Citation Index Expanded
- Citazioni:
- 25
- Recensione:
- Indirizzi per estratti:
-
-
-
- Citazione:
- J. Kunze e I. Rothe, "SOLUBILITY OF NITROGEN IN AUSTENITIC FECRMN ALLOYS", Steel research, 65(8), 1994, pp. 331-337
Abstract
The equilibrium solubility of nitrogen in austenitic iron-chromium, iron-manganese, and iron-chromium-manganese alloys with mass up to 20 %Cr and 18 % Mn was measured in the temperature range 1273 to 1473 K. The following interaction parameters were obtained: [GRAPHICS] Describing the effect of chromium and/or manganese on the nitrogen solubilityby the excess term G(N)E - RTepsilon(N)(N)s(N), the present measurements correspond satisfactorily to those of Hertzmann and Jarl and of Zheng in the system Fe-Cr-N, but they differ somewhat from values calculated by means of parameters published by Frisk. For the system Fe-Mn-Nthe present measurements correspond to measurements by Grabke et al. and to values calculated with parameters published by Qiu. Using parameters deduced from the present measurements in the austenitic Fe-Cr-Mn-N system similar nitrogen solubilities were calculated as Zheng had measured, but small deviations were found between the analysis by Qiu and this investigation.